The aim of present work is to improve mechanical and fatigue properties for Aluminum alloy7049 by using Nano composites technique. The ZrO2 with an average grain diameter of 30-40 nm, was selected as Nano particles, to reinforce Aluminum alloy7049 with different percentage as, 2, 4, 6 and 7 %. The Stir casting method was used to fabricate the Nano composites materials due to economical route for improvement and processing of metal matrix composites. The experimental results were shown that the adding of zirconium oxide (ZrO2) as reinforced material leads to improve mechanical properties. The best percentage of improvement of mechanical properties of 7049 AA was with 4% wt. of ZrO2 about (7.76% ) for ultimate tensile stress UTS, (9.62% ) for yield stress YS and (9.92%) for hardness HB than other of adding of 2, 6 and 7% of ZrO2. Also the results shown that the fatigue strength of 7049 AA with 4 % ZrO2 nanoparticles is higher than that of 7049 AA under constant loading 9.86% at 108 cycles as well as the fatigue life factor (IFLF %) at different amplitude stress 400, 350, 300 and 250 MPa was improvement in range 66, 115, 63 and 107% respectively.
Copyright: Open Access authors retain the copyrights of their papers, and all open access articles are distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution and reproduction in any medium, provided that the original work is properly cited. The use of general descriptive names, trade names, trademarks, and so forth in this publication, even if not specifically identified, does not imply that these names are not protected by the relevant laws and regulations. While the advice and information in this journal are believed to be true and accurate on the date of its going to press, neither the authors, the editors, nor the publisher can accept any legal responsibility for any errors or omissions that may be made. The publisher makes no warranty, express or implied, with respect to the material contained herein.
 Koji Takahashi, Hiroko Osedo, Takaya Suzuki, Shinsaku Fukuda, "Fatigue strength improvement of an aluminum alloy with a crack-like surface defect using shot peening and cavitation peening" Engineering fracture Mechanics, vol. 193, pp. 151-161, April 2018.
 Abdul-Jabar H. Ali, "Improvement of Fatigue Life of AA 7075 Using Laser Shock Peening (LSP) Surface Treatment Technique", Al-TAQANI Refereed Scientific Journal, vol. 29, pp. 47-57 (2016).
 Dorman, M., Toparli, M. B., Smyth, N., Cini, A., Fitzpatrick, M. E. and Irving, “Effect of laser shock peening on residual stress and fatigue life of clad 2024 aluminum sheet containing scribe defects”, Materials Science and Engineering: A, 548, pp. 142–151, (2012).
 M. Dinesh, R.Ravindran "Tensile and hardness behavior of aluminum 7075 and Zinc and Chromium metal matrix composite by Stir-Casting Route" International Archive of applied Sciences and Technology , vol. 7 , pp. 39- 46 (2016).
 C. Kannan, R. Ramanujam," Comparative study on the mechanical and microstructural characterisation of AA 7075 nano and hybrid nanocomposites produced by stir and squeeze casting" Contents lists available at Science Direct Journal of Advanced Research 309–319 8 (2017).
 S. Divagar, M. Vigneshwar, S.T. Selvamani " Impacts of Nano Particles on Fatigue Strength of Aluminum Based Metal Matrix Composites for Aerospace" Materials Today: Proceedings, vol. 3, pp. 3734-3739, (2016).
 S.E.Shin, D.H.Bae," Fatigue behavior of Al2024 alloy-matrix nanocomposites reinforced with multi-walled carbon nanotubes" Science Direct, Composites Part B: Engineering Volume 134, , Pages 61-68, (1 February 2018).
 Al-Alkawi H.J. M., Ibtihal A. M., Mamoon A. A. Al- Jaafari," An Estimation Study on Fatigue Transition Life of Nanocomposites Reinforced by Al203"Arab universities union general secretary of Arab engineering colleges society, (2017).
 A.P. Utkarsh Prajapati, A.P. Jay H Patel, Ketul V Patel, Parthkumar P Patel, Pujan P Bhatt, Sandipkumar O Varma," Effect ofAl2O3Nano-ParticleonMechanical Properties of Aluminum Based Alloy: A Review", IOSR Journal of Mechanical and Civil Engineering (IOSR-JMCE) e-ISSN: 2278-1684, p-ISSN: 2320-334X, Volume 13, Issue 2 Ver. II, PP 72-75, (Mar. - Apr. 2016)
 Al-Alkawi H.J.M., Abthal A. M., Mamoon A. A. Al- Jaafari," Mechanical Properties of 7075 Aluminum Alloy Matrix/Al2O3, Particles Reinforced Composites" Engineering and Technology journal, (2017).
 R. Senthilkumar, N. Arunkumar, M. Manzoor Hussian,"Comparative Study on Low Cycle Fatigue Behaviour of Nano and Micro A1203 Reinforced AA2oI4 Particulate" Hybrid Composites Results in Physics, vol. 5, pp. 273-280 (2015).
 Al-Alkawi H.J.M., Ibtihal A. M., Mamoon A. A. Al- Jaafari," Fatigue life Study on 7075 Aluminum Alloy matrix / nanoparticles Al2O3 reinforced composite" The Iraqi Journal for mechanical and materials Engineering (2017).
 Hajizamani, Hamidreza Baharvandi" Fabrication and studying the mechanical properties of A356 alloy reinforced with Al2O3-10% Vol. ZrO2 nanoparticles through stir casting" Advances in Materials Physics and Chemistry, vol. 1, pp. 26-30 (2011).
 Ali Mazahery1 and Mohsen Ostadshabani, "Investigation on mechanical properties of nano-Al2O3-reinforced aluminum matrix composites "Journal of Composite Materials 45(24) 2579–2586, (2011).
 Sharp P. K., Barter S. A. and Clark G., "Localized life extension specification for the F/A-18. Y470x19 pocket", Melbourne: DSTO-TN-0279, (2000).
 Abdizadeh H., Baghchesara M.A., "Investigation into mechanical properties and fracture behavior of A356 aluminum alloy-based ZrO2 particle reinforced metal matrix composites" Mechanics of composite materials, Vol.49, No.5 (2013).